00000ctm a22000003a 4500 UP-1685523046126209182 Buklod 20110204111241.0 m |o d | cr ||||||||||| 110204s xx d r |||| u| (iLib)UPMNL-00011581156 UPDent eng LG 995.3 2010 D4 P33 Padua, Ana Rose P. Marginal sealing property of temporary restorative materials A comparative study Ana Rose P. Padua, Roderick C. Perez, Vicente O. Medina III. vii 42 leaves Seminar Paper--Doctor of Dental Medicine--University of the Philippines Manila. Objective: This study aims to compare the marginal sealing property Provifil (Promedica, Germany), a new light-cured one-component temporary filling material with IRM (Dentsply-Caulk) and Cavit (3M ESPE). Methodology: Standard box-shaped cavity preparations were completed in forty (40) caries-free anterior bovine teeth. The teeth were randomly assigned to 4 groups (n=10) and were filled with one of the three restorative materials. In five teeth (Positive control), no restorative material was placed; while five teeth of the negative control group had no restorative material but were filled with sticky wax. After thermocycling in water baths with temperatures of 5±5°C and 55±5°C (dwell time, 30 seconds) for 200 cycles, the teeth were coated with nail varnish, leaving an area of 1 mm short of the cavity margin uncovered. The samples were immersed in 2% Methylene blue dye solution for 10 days, then sectioned and digital pictures were taken. Dye penetration along the walls was measured using the UTHSCA Image Tool software. The greatest depth of dye penetration was considered the score of the specimen. Data was analyzed using One-way ANOVA (ρ < 0.05) and Turkey's HSD Post Hoc Test. Results: All the materials tested leaked at the tooth-restorative material interface. Provifil had the lowest mean leakage value (1.609 mm) while Cavit had the next lowest (2.028 mm). IRM demonstrated significant leakage values (4.587 mm) signifying complete dye penetration on all the samples. Conclusion: There was no statistically significant difference between the marginal sealing property of Cavit and Provifil (ρ>0.05). The marginal sealing property of Provifil was better than that of IRM. Dental materials. Perez, Roderick C. Medina, Vicente O. (Co-author). Rosanes, Rose Anne Q. (Adviser). UPMNL DENT LG 995.3 2010 D4 P33 Thesis